Methods of cementing with lightweight cement compositions

ABSTRACT

Foamed cement compositions comprising density reducing additives and methods of making and using the same are disclosed. In one embodiment, a method of cementing is disclosed. The method of cementing comprises preparing a base cement composition comprising a cement, a water, and a density reducing additive, wherein the base cement composition comprises a base density. The method further comprises introducing a gas to the base cement composition to provide a cement composition having a density less than the base density and allowing the cement composition to set.

CROSS-REFERENCE TO RELATED APPLICATIONS

Not applicable.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

Not applicable.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to the field of cementing operations and morespecifically to the field of using lightweight foamed cementcompositions comprising density reducing additives to service awellbore.

2. Background of the Invention

Natural resources such as gas, oil, and water residing in a subterraneanformation or zone are usually recovered by drilling a wellbore down tothe subterranean formation while circulating a drilling fluid in thewellbore. After terminating the circulation of the drilling fluid, astring of pipe, e.g., casing, is run in the wellbore. The drilling fluidis then usually circulated downward through the interior of the pipe andupward through the annulus, which is located between the exterior of thepipe and the walls of the wellbore. Next, primary cementing is typicallyperformed whereby a cement slurry is placed in the annulus and permittedto set into a hard mass (i.e., sheath) to thereby attach the string ofpipe to the walls of the wellbore and seal the annulus. Subsequentsecondary cementing operations may also be performed. One example of asecondary cementing operation is squeeze cementing whereby a cementslurry is employed to plug and seal off undesirable flow passages in thecement sheath and/or the casing.

In some environments, cementing operations may need lightweight cementslurries having reduced densities (e.g., a low-density slurry). Forinstance, cementing across highly depleted zones and weaker formationsmay need a lightweight cement for sufficient circulation. If the cementcannot be successfully circulated, the desired level of annular fill maynot be achieved, and consequently the desired seal may not be achieved.As a result, a large impact on the drilling cost may be experienced anddelays in production delivery may occur due to the remedial work.

Lightweight cements are typically prepared by addition of water,microspheres or gas to the cement. Drawbacks to addition of extra waterto the cement include reduced efficiency in solidifying of the cement.For instance, the additional water may dilute the cement and therebyextend the time at which the cement may set. Drawbacks to usingmicrospheres include costs associated in adding a sufficient amount ofmicrospheres to reduce the density of the cement to lower than typicaldensities. Drawbacks to adding gas include excess permeability at highgas concentrations.

Consequently, there is a need in the art for an improved method ofpreparing a lightweight cement and for cementing with compositionsthereof. Other needs include a lightweight cement having improvedmechanical properties. In addition, needs in the art include alightweight cement having a reduced density.

BRIEF SUMMARY OF SOME OF THE PREFERRED EMBODIMENTS

These and other needs in the art are addressed in one embodiment by amethod of cementing that includes preparing a base cement compositioncomprising a cement, a water, and a density reducing additive, whereinthe base cement composition comprises a base density. The method furtherincludes introducing a gas to the base cement composition to provide acement composition having a density less than the base density andallowing the cement composition to set.

In another embodiment, needs in the art are addressed by a method forreducing the density of a cement composition. The method includesselecting a target density of the cement composition. In addition, themethod includes forming the cement composition having a first densitygreater than the target density by a density factor, wherein the cementcomposition comprises a cement, a water, and a density reducingadditive. The method further includes adding a sufficient amount of agas to the cement composition to reduce the first density to about thetarget density.

Needs in the art are addressed in another embodiment comprising a cementcomposition that has water, cement, a density reducing additive, and agas. The cement composition has a density from about 5 pounds per gallonto about 7.5 pounds per gallon.

A cement composition comprising water, cement, a density reducingadditive, and a gas overcomes problems in the art such as reducing thedensity of conventional cement compositions to low densities. Forinstance, the density of such a cement composition may be reduced tolower than typical densities. In addition, such a cement composition canhave improved mechanical properties (e.g., compressive strength andelasticity) at reduced densities.

The foregoing has outlined rather broadly the features and technicaladvantages of the present invention in order that the detaileddescription of the invention that follows may be better understood.Additional features and advantages of the invention will be describedhereinafter that form the subject of the claims of the invention. Itshould be appreciated by those skilled in the art that the conceptionand the specific embodiments disclosed may be readily utilized as abasis for modifying or designing other structures for carrying out thesame purposes of the present invention. It should also be realized bythose skilled in the art that such equivalent constructions do notdepart from the spirit and scope of the invention as set forth in theappended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

For a detailed description of the preferred embodiments of theinvention, reference will now be made to the accompanying drawings inwhich:

FIG. 1 illustrates an example of a predicted density profile for astaged constant gas rate low-density foamed cement composition;

FIG. 2 illustrates a predicted density profile of another low-densityfoam cement composition; and

FIG. 3 illustrates a 5.0 lb/gal cement crush-test chart.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

In an embodiment, a cement composition comprises cement, water, adensity reducing additive, and a gas. The gas is introduced to a cementcomposition comprising cement, water, and a density reducing additive toprovide a foamed cement composition (e.g., a lightweight cementcomposition). In an embodiment, the foamed cement composition is alow-density cement composition. Without being limited by theory, foaminga cement composition comprising density reducing additives provides alow-density cement composition with improved mechanical properties atlow densities. Low-density cement compositions refer to cementcompositions having a density less than about 14 lb/gallon. It is to beunderstood that foaming the cement composition comprising densityreducing additives is not limited to providing a low-density cementcomposition but in alternative embodiments can provide a cementcomposition with a density of about 23 lb/gallon or less.

The cement compositions are suitable for subterranean applications suchas well completion and remedial operations. It is to be understood that“subterranean applications” encompass both areas below exposed earth andareas below earth covered by water such as ocean or fresh water.

The cement composition comprises a cement such as hydraulic cement,which includes calcium, aluminum, silicon, oxygen, and/or sulfur andwhich sets and hardens by reaction with water. Examples of hydrauliccements include but are not limited to Portland cements (e.g., classesA, C, G, and H Portland cements), pozzolana cements, gypsum cements,phosphate cements, high alumina content cements, silica cements, highalkalinity cements, and combinations thereof.

In some embodiments, the cement compositions include a sufficient amountof water to form a pumpable cementitious slurry. The water may be freshwater or salt water, e.g., an unsaturated aqueous salt solution or asaturated aqueous salt solution such as brine or seawater, or anon-aqueous fluid. The water may be present in the amount from about 20to about 180 percent by weight of cement, alternatively from about 28 toabout 60 percent by weight of cement.

The cement composition comprises a sufficient amount of the densityreducing additives to reduce the density of the cement composition. Thecement composition may include density reducing additives that arecompatible with a subterranean cement composition (i.e., that arechemically stable at least until the cement sets). Without limitation,examples of density reducing additives include hollow glass beads,pozzolanic microspheres, solid beads (e.g., solid organic or plasticbeads), or combinations thereof.

An example of a suitable hollow glass bead is commercially availablefrom 3M Company as SCOTCHLITE. An example of a suitable microsphere iscommercially available from Halliburton Energy Services, Inc. asSPHERELITE. In addition, an example of a suitable solid bead iscommercially available from Halliburton Energy Services, Inc. asFDP-C665. The density reducing additives may be added to the cementcomposition by any suitable method including dry blending with thecement before the addition of water, mixing with the water to be addedto the cement, or by mixing with the cement slurry consecutively with orafter the addition of the water. In another embodiment, the densityreducing additives may be pre-suspended in water and injected into thecement mix fluid or into the cement slurry as an aqueous slurry.

The gas may include any gas suitable for foaming the cement compositionand for use in a wellbore. Without limitation, examples of suitablegases include nitrogen, air (e.g., compressed air), or combinationsthereof. In some embodiments, the gas is nitrogen. The gas may beintroduced to the cement composition by any method suitable to foam thecement composition. In addition, the gas may be introduced at a constantrate or a ramped rate to yield a constant downhole foam concentration ordensity. In an embodiment, introducing the gas into the cementcomposition to foam the cement composition may be accomplished by addingan expanding agent comprising foaming agents, foam stabilizing agents,expanding additives, or combinations thereof to the cement composition,which may be included in the cement composition to facilitate thefoaming and/or enhance the stability of the cement composition. Suchfoaming and/or foam stabilizing agents may be present in the cementcomposition in an amount sufficient to provide a stable, foamed cementcomposition. It is to be understood that one of ordinary skill in theart would be able to select the proper foaming and/or foam stabilizingagents according to the particular application.

In an embodiment, the cement composition includes an expanding additive.The expanding additive may be any component that enables a gas to becomeincorporated into the cement composition. Without limitation, examplesof suitable expanding additives in particulate form include aluminumpowder, gypsum blends, deadburned magnesium oxide, and combinationsthereof. Examples of expanding additives comprising aluminum powder thatare commercially available include GAS-CHEK and SUPER CBL fromHalliburton Energy Services, Inc. An example of an expanding additivecomprising a blend containing gypsum is commercially available asMICROBOND from Halliburton Energy Services, Inc. In addition, examplesof expanding additives comprising deadburned magnesium oxide arecommercially available as MICROBOND M and MICROBOND HT from HalliburtonEnergy Services. Inc. Such expanding additives are described in U.S.Pat. Nos. 4,304,298; 4,340,427; 4,367,093; 4,450,010 and 4,565,578,which are incorporated herein by reference in their entirety.

The addition of an expanding additive to the cement composition may beaccomplished by any suitable method. In one embodiment, the cementcomposition is foamed by direct injection of an expanding additive intothe cement composition. For instance, where the cement composition isfoamed by the direct injection of gas into the cement composition, thegas utilized may be air, an inert gas such as nitrogen, or combinationsthereof. In other embodiments, the cement composition is foamed by gasgenerated from a reaction between the cement composition and anexpanding additive present in the cement composition in particulateform. For example, the cement composition may be foamed by hydrogen gasgenerated in situ as the product of a reaction between the high pHslurry and fine aluminum powder present in the cement.

The cement composition is prepared to have a density at about a targetdensity. In an embodiment, the cement composition is prepared or placedin a wellbore and has a density (e.g., target density) less than aboutthat of a fracture gradient in the wellbore. The fracture gradientrefers to the force that induces rock to fracture at a given depth. Thevariability of the fracture gradient for a given wellbore as a functionof depth may be graphed and may be referred to as a fracture gradientprofile. The density of the cement composition can be predicted andplotted as a downhole density profile. In another embodiment, the cementcomposition has a density (e.g., target density) from about 4 to about14 lb/gallon, alternatively from about 5 to about 7.5 lb/gallon, andalternatively from about 5 to about 6 lb/gallon. In an alternativeembodiment, the cement composition has a density from about 7.5lb/gallon to about 12 lb/gallon.

The cement composition is prepared by selecting a target density atwhich the cement composition is to be circulated. It is to be understoodthat the target density may be selected based upon factors such as theparticular application, wellbore environment, and the like. A basecement composition is then prepared having a base density that isgreater than the target density by a density factor. The base cementcomposition comprises water, cement, and a density reducing additive.The density factor is a numerical factor applied to the selected targetdensity to increase the target density to the base density and therebyallowing sufficient quantities of gas to then be added to provide thedesired downhole properties. The density factor may be selected basedupon factors such as desired downhole properties of elasticity,cohesion, or compressibility In an embodiment, the density factor isfrom about 1.01 to about 1.4, alternatively 1.01 to about 1.3, furtheralternatively from about 1.2 to about 1.3, and alternatively about 1.25.To prepare the base cement composition, a sufficient amount of thedensity reducing additives are added to a slurry comprising cement andwater to reduce the density of the slurry and provide the base cementcomposition having a density at about the desired base density. The basecement composition may then be foamed by introducing the gas to the basecement composition. A sufficient amount of the gas is added to reducethe density of the base cement composition and provide the cementcomposition with a density at about the target density. It is to beunderstood that the target density may be the final density at which thecement composition can be safely circulated in the wellbore. In anembodiment, the cement composition comprises from about 10 to about 30vol. % gas, alternatively from about 20 to about 30 vol. % gas, andalternatively from about 25 to about 30 vol. % of the gas. It is to befurther understood that a sufficient amount of the expanding agent maybe added to the cement composition to provide the amount of gas suitablefor achieving the target density.

In one embodiment, the base density and downhole density profile may bedetermined utilizing a computer simulation program. In an embodiment,the percent volume of gas in the cement slurry is monitored in real-timeusing a software program. Alternatively, the downhole density profileand real-time monitoring of the percent volume of gas addition to thecement slurry is automatically controlled and monitored utilizing acomputer and appropriate simulation and automation software. Softwarefor monitoring the percent volume of gas addition to the base cementcomposition may function to identify the composition rate and calculatethe proper gas injection rate based on the actual composition rate andpredetermined target density. In some embodiments, the softwarefunctions as a component of an automated gas introduction device thatsynchronizes the gas injection rate with the cement slurry concentrationrate to achieve the target density. Examples of suitable softwareinclude but are not limited to HALWIN or INSITE, which are commerciallyavailable from Halliburton Energy Services, Inc. In an embodiment, thecomputer is a digital computer such as an IBM Intel Pentium-basedpersonal computer capable of receiving input from multiple detectorsthrough serial interfaces. The computer may also be capable of receivinginput through a standard keyboard or another computer.

Without being limited by theory, foaming a cement composition comprisingdensity reducing additives provides a low-density cement compositionhaving improved mechanical properties. Mechanical properties of thecement composition that may be improved by foaming the cementcomposition comprising density reducing additives include withoutlimitation compressibility and elasticity. Metrics utilized to defineelasticity include Poisson's ratio and Young's modulus.

Poisson's ratio refers to the ratio of transverse contraction strain tolongitudinal strain in the direction of stretching force and isrepresented by the following Equation (1):ν=ε_(transverse)/ε_(longitudinal)  (1)wherein ν represents Poisson's ratio and ε represents strain as definedby the charge in length divided by the original length. Young's modulus,λ, is indicative of the elasticity of a material or the tendency of thematerial to deform under an applied force. Young's modulus isrepresented by the following Equation (2):λ=(F/A)/(x/l)  (2)where F is the applied force, A is the area to which the force isapplied, X is the extension of the material when the force is appliedand 1 is the original length of the material.

In an embodiment, the cement compositions may have a compressivestrength between about 200 psi and about 3,000 psi, alternativelybetween about 500 psi and about 1,500 psi. In other embodiments, thecement compositions may have a tensile strength between about 30 psi andabout 500 psi, alternatively between about 50 psi and about 150 psi.Moreover, the cement compositions may have a Young's modulus betweenabout 60,000 and about 6,000,000, alternatively between about 200,000and about 900,000.

It is to be understood that preparation of the cement composition is notlimited to foaming a base cement composition comprising density reducingadditives but instead may include adding density reducing additives to afoamed cement. For instance, in an alternative embodiment, a base cementcomposition can be prepared with a base density by foaming a cementslurry comprising cement and water. In such an alternative embodiment,the base cement composition comprises water, cement, and a gas. Thelow-density cement composition is then prepared by adding the densityreducing additives to the base cement composition to provide thelow-density cement composition having about the target density.

In some embodiments, additional additives may be added to the cementcomposition for improving or changing the properties thereof. Examplesof such additives include but are not limited to salts, accelerants, setretarders, defoamers, fluid loss reducing agents, settling preventionagents, gas migration prevention additives, weighting materials,dispersants, vitrified shale, formation conditioning agents, andcombinations thereof. Other mechanical property modifying additives, forexample, carbon fibers, glass fibers, metal fibers, minerals fibers,thermoplastic elastomers such as styrene butadiene oracrylonitrile-styrene-butadiene random or block polymers, and latexemulsions, for example styrene-butadiene latexes, and the like can beadded to further modify the mechanical properties.

The foregoing cement compositions may be used in various cementingoperations wherein the cement is displaced into a workspace and allowedto set. In an embodiment, the cement compositions are used in varioussurface applications to cement a workspace at or above the ground, forexample, a workspace encountered in the construction industry. Inanother embodiment, the cement is used in a subterranean workspace, forexample in cementing underground pipe such as sewer pipe or wellborecasing. In one embodiment, the cement compositions may be employed inprimary cementing of a wellbore for the recovery of natural resourcessuch as water or hydrocarbons. Primary cementing first involves drillinga wellbore to a desired depth such that the wellbore penetrates asubterranean formation while circulating a drilling fluid through thewellbore. Subsequent to drilling the wellbore, at least one conduit suchas a casing may be placed in the wellbore while leaving a space known asthe annulus between the wall of the conduit and the wall of thewellbore. The drilling fluid may then be displaced down through theconduit and up through the annulus one or more times, for example,twice, to clean out the hole. The cement composition may then beconveyed downhole and up through the annulus, thereby displacing thedrilling fluid from the wellbore. The cement composition sets into ahard mass, which forms a cement column that isolates an adjacent portionof the subterranean formation and provides support to the adjacentconduit.

In another embodiment, the cement composition may be employed in asecondary cementing operation such as squeeze cementing, which isperformed after the primary cementing operation. In squeeze cementing,the cement composition is forced under pressure into permeable zonesthrough which fluid can undesirably migrate in the wellbore. Examples ofsuch permeable zones include fissures, cracks, fractures, streaks, flowchannels, voids, high permeability streaks, annular voids, orcombinations thereof. The permeable zones may be present in the cementcolumn residing in the annulus, a wall of the conduit in the wellbore, amicroannulus between the cement column and the subterranean formation,and/or a microannulus between the cement column and the conduit. Thecement composition sets within the permeable zones, thereby forming ahard mass to plug those zones and prevent fluid from leakingtherethrough.

To further illustrate various illustrative embodiments of the presentinvention, the following examples are provided.

EXAMPLES Example 1

Seven wells were drilled with the following procedures: 20 inch surfacecasing was set down to 541 ft, 394 ft of a 13⅜-in. scab liner was set to1,378 ft, a 9⅝-in. intermediate string was set to 1,545 ft, and a 7-in.production string was set at 2,756 ft. The upper formations were suchthat successful cementing could be accomplished with conventionalcementing techniques. However, the intermediate and production stringswere to be cemented past zones that required cement densities to bereduced to 10.6 lb/gal or less. 13.6 lb/gal was chosen as the baseslurry density so that when the target density was attained, the foamquality (e.g., vol. % of foam in the cement composition) would bebetween 20 and 25%. The target density was 10.6 lb/gal and was chosen toallow successful circulation of a full cementing column. Microsphereswere added to the base slurry to provide the base cement compositionwith a density of 13.6 lb/gal. The microspheres were HGS-4000 glassbubbles from 3M, which were intermediate-strength glass microsphereswith a specific gravity of 0.38.

The entire process was monitored in real-time using a software program,HALWIN, and a correct amount of nitrogen was added to the base cementcomposition at each stage using an adjustable choke. The choke wasadjusted until the surface foam density matched the calculated densityfor that rate and pressure. The low-density base cement composition wasused as the tail, without gas in the process.

For the 9⅝-in. string, 267.3 bbl of unfoamed cement composition, 13.6lb/gal lead slurry and 22.6 bbl of tail slurry were used. Thetheoretical in-place foam volume for the lead slurry was 347.8 bbl (at10.6 lb/gal). For the 7-in. string, 96.2 bbl of lead slurry, and 3.1 bblof tail slurry were used. The theoretical in-place foam volume for thelead slurry was 125.8 bbl.

A computer simulation program, OPTICEM commercially available fromHalliburton Energy Services, Inc., was used to engineer the backpressureand nitrogen schedules. FIGS. 1 and 2 display the theoretical in-placedensity profiles for the 9⅝-in. and 7-in. jobs, respectively. Thesecurves indicated that by reducing the nitrogen rate four and five times,respectively, the specific gravity of the foam would be maintainedbetween 1.2 and 1.3 (10-10.8 lb/gal), for most of the well, whichcorrelated to the desired foam quality of 20 to 25%. It can also be seenin FIGS. 1 and 2 that expansion occurs more rapidly as the surface wasapproached. To minimize expansion, cementing software allowed theback-pressure schedule to be adjusted as needed

Table I provides the planned back-pressure schedules for the two foamedcasing strings. As the foam was placed up the annulus, moreback-pressure was applied. To better control downhole rate and slurryconsistency, a 100-bbl batch mixer was included in the job procedure.TABLE I Back-Pressure Schedule for Wells 9⅝-in. Intermediate Casing Job7-in. Production Casing Job Backpressure (psi) Backpressure (psi) 14.714.7 90 65 115 100 140 125 165 N/A

Example 2

Thirteen Runs were performed (Runs 1-13) with foamed cement compositionscomprising cement, water, microspheres, and gas. The foamed cementcompositions were prepared by mixing a base cement compositioncomprising water, cement, and microspheres to have a density between 10and 12 lb/gal. The base cement composition was foamed to a density of8.33 lb/gal with about 50-600 scf/bbl of nitrogen.

Table II lists data related to the wells drilled in Runs 1-13. Table IIIlists the amounts and densities of the base cement compositions and thefoamed cement compositions used in the Runs. TABLE II Foamed LightweightSlurry Cemented Well Data Liner Job Size Depth BHST RUNS (in.) (ft) (°F.) 1 7 14632 273 2 7 13760 255 3 7 11647 226 4 7 14964 258 5 5 14902275 6 5 13409 222 7 7 13638 256 8 7 14577 269 9 7 14862 270 10 7 14606246 11 7 13596 250 12 7 12477 207 13 5 14980 267

TABLE III Foamed Lightweight Cement Job Data Base Slurry Foamed SlurryBase In-Place Volume Volume Density Foam Density Runs (bbl) (bbl)(lb/gal) (lb/gal) 1 25 36 15 10.8 2 33 48 15 10.8 3 38.8 59 11.7 8.33 450.5 72 10.8 8.33 5 34.8 49.1 10.8 8.33 6 16.9 23.2 10.8 8.33 7 51 72.510.8 8.33 8 32.3 49.7 11.7 8.33 9 43.4 67.4 11.7 8.33 10 56 86 11.7 8.3311 36.7 56.3 11.7 8.33 12 49 76 11.7 8.33 13 20 31 11.7 8.33

The 13 liner tops cemented in this Example 2 were tested to an averagepressure of 1,400 psi for 20 minutes, without leaking. Initial andactual production rates before and after well stimulation as shown inTable IV for Runs 3-5 and 7-10 illustrate the effectiveness of thesealing capability and chemical attack resistance of the foamed cementcompositions. The effectiveness of the seal achieved utilizing themethods and compositions disclosed was further illustrated by theability of the wells to undergo subsequent fracturing treatments. TABLEIV Foamed Lightweight Cement Before-and-After Production Rates InitialPay Zone Depth Production Actual Production RUNS (ft) (BOPD) (BOPD) 312,795-12,936 618 1,352 4 14,180-14,305 0 1,258 5 14,518-14,419 1,0061,635 7 12,999-13,097 0 566 8 14,206-14,337 0 1,541 9 14,623-14,741 01,793 10 14,058-14,222 0 1,182

Example 3

A 7.5-lb/gal base cement composition was foamed down to 5 lb-/gal toproduce a sealant quality low-density cement composition. The basecement composition and low density cement compositions were subjected totests of fluid loss thickening time, free water and compressivestrength. The tests were conducted according to API 10b procedures. At212° F., the base slurry yielded 1,369-psi compressive strength, andafter being foamed down to 5 lb/gal still yielded 703-psi 24-hourcompressive strength. FIG. 3 illustrates a crush test implemented on thefoamed cement composition after it was set.

While preferred embodiments of the invention have been shown anddescribed, modifications thereof can be made by one skilled in the artwithout departing from the spirit and teachings of the invention. Theembodiments described herein are exemplary only, and are not intended tobe limiting. Many variations and modifications of the inventiondisclosed herein are possible and are within the scope of the invention.Use of the term “optionally” with respect to any element of a claim isintended to mean that the subject element is required, or alternatively,is not required. Both alternatives are intended to be within the scopeof the claim. Use of broader terms such as comprises, includes, having,etc. should be understood to provide support for narrower terms such asconsisting of, consisting essentially of, comprised substantially of,etc.

Accordingly, the scope of protection is not limited by the descriptionset out above but is only limited by the claims which follow, that scopeincluding all equivalents of the subject matter of the claims. Each andevery claim is incorporated into the specification as an embodiment ofthe present invention. Thus, the claims are a further description andare an addition to the preferred embodiments of the present invention.The discussion of a reference in the Description of Related Art is notan admission that it is prior art to the present invention, especiallyany reference that may have a publication date after the priority dateof this application. The disclosures of all patents, patentapplications, and publications cited herein are hereby incorporated byreference, to the extent that they provide exemplary, procedural orother details supplementary to those set forth herein.

1. A method of cementing, comprising: preparing a base cementcomposition comprising a cement, a water, and a density reducingadditive, wherein the base cement composition comprises a base density;introducing a gas to the base cement composition to provide a cementcomposition having a density less than the base density; and allowingthe cement composition to set.
 2. The method of claim 1, wherein thedensity is from about 5 to about 7.5 pounds per gallon.
 3. The method ofclaim 1, wherein the cement composition comprises from about 10 to about30 volume percent of the gas.
 4. The method of claim 1, wherein thecement composition has a compressive strength from about 200 to about3,000 psi.
 5. The method of claim 1, wherein the density reducingadditive comprises hollow glass beads, pozzolanic microspheres, solidbeads, or combinations thereof.
 6. The method of claim 1, wherein thecement composition is prepared by: selecting a target density of thecement composition, wherein the target density is about the density ofthe cement composition; forming the base cement composition having thebase density greater than the target density by a density factor; andadding a sufficient amount of the gas to the base cement composition toform the cement composition having about the target density.
 7. Themethod of claim 6, wherein the density factor is from about 1.01 toabout 1.4.
 8. The method of claim 1, wherein the cement composition isplaced in a wellbore.
 9. The method of claim 8, wherein the density isless than about a fracture gradient of the wellbore.
 10. The method ofclaim 1, wherein the gas comprises nitrogen.
 11. A method for reducing adensity of a cement composition, comprising: selecting a target densityof the cement composition; forming the cement composition, wherein thecement composition has a first density greater than the target densityby a density factor, and wherein the cement composition comprises acement, a water, and a density reducing additive; and adding asufficient amount of a gas to the cement composition to reduce the firstdensity to about the target density.
 12. The method of claim 11, whereinthe target density is from about 5 to about 7.5 pounds per gallon. 13.The method of claim 11, wherein the target density is from about 7.5 toabout 12 pounds per gallon.
 14. The method of claim 11, wherein thecement composition comprising about the target density comprises fromabout 10 to about 30 volume percent of the gas.
 15. The method of claim11, wherein the cement composition comprising about the target densityhas a compressive strength from about 200 to about 3,000 psi.
 16. Themethod of claim 11, wherein the density reducing additive compriseshollow glass beads, pozzolanic microspheres, solid beads, orcombinations thereof.
 17. The method of claim 11, wherein the densityfactor is from about 1.01 to about 1.4.
 18. The method of claim 11,wherein the cement composition is placed in a wellbore, and wherein thetarget density is less than about a fracture gradient of the wellbore.19. A cement composition comprising a water, a cement, a densityreducing additive, and a gas, wherein the cement composition has adensity from about 5 pounds per gallon to about 7.5 pounds per gallon.20. The cement composition of claim 19 comprising from about 10 to about30 volume percent of the gas.